Distractum chalybis perforatum polyethylenum compositum e fimbriis frigido-volutis et thermoplasticis sicut materias rudis facta est, et fistulis raris tenuissimis ferro munitae, quae ab argonis arcu glutino vel plasmate spirae glutino adhibitae sunt subsidia. Strati exteriores et interiores thermoplastici sunt duplex postesque compositi. Novum genus pressionis compositae organi compositi, quia fistula raris tenuibus vallata subsidiis thermoplasticis continuis involvitur, haec composita fistula non solum defectus fistulae ferri et fistulae plasticae vincit, sed etiam rigiditatem fistulae ferreae et corrosionem habet. resistentia fistulae plasticae. Solutio petrolei et chemicae industriarum est. Enixe opus est pipelino magni et medii diametri fistulae rigidae in campis pharmaceuticae, cibi, fodiendi, gasi et aliorum agrorum. Est etiam res technologica revolutionalis ad solvendum principale pipeline constructionis et copia aquae municipalis. Novum genus compositorum pipeline in 21stsaec.
Features
Altae roboris et humilis expansio linearis.
Ob roborationem de chalybeis, habena ferrata perforata fistulae plasticae compositae maiorem vim habet, altam rigiditatem et impulsum resistentiae quam fistulae plasticae. Eodem tempore, refrenatio effectus chalybis frame etiam facit habenam perforati plastici fistulae compositae, habent lineam humilem similem fistulae ferreae. Expansio coefficiens et сгеер resistentia.
Erugo et indue resistentia.
Summus densitas polyethylene materia electa ad habena ferro perforato fistulae plasticae compositae est cristallina polymerus non-polaribus cum proprietatibus chemicis stabilibus, resistentia maxime acido, salibus alcali et instrumentis organicis, et corrosio electrochemico. Molestas operandi 5 temporibus altior est quam ferreis fistulis.
Technical Parameters
Hoc productum utitur resina polyethylene speciali, et eius proprietatibus physicis et mechanicis occurrit in Ministerio constructionis vexillum CJ/T181-2003 et chemicae industriae vexillum HG/T3706-2014.
| Specificatio magnitudinis, deviationis et pressionis nominalis: requisitis ministerii constructionis vexillum CJ/T181-2003 | |||||
| Nominal diametri exterioris et declinationis | Crassitudo muri nominal et declinatio | De rotunditate | Pressura nominatim | Minimum S valorem | Longitudo et declinatio |
| Dn(mm) | En(mm) | Mm | Mpa | Mm | mm |
| 50+0.5 0 | 4.0+0.5 9 | 1.0 | 2.0 | 1.5 | 6000+20 0 9000+20 0 12000+20 0 |
| 60+0.6 0 | 4.5+0 | 1.26 | 2.0 | 1.5 | |
| 75+0.7 0 | 5.0+0 | 1.5 | 2.0 | 1.5 | |
| 90+0.9 0 | 5.5+0 | 1.8 | 2.0 | 1.5 | |
| 110+1.0 0 | 6.0+0.9 0 | 2.2 | 2.0 | 1.5 | |
| 140+1.1 0 | 8.0+1.0 0 | 2.8 | 1.6 | 2.5 | |
| 160+1.2 0 | 10.0+1.1 0 | 3.2 | 1.6 | 2.5 | |
| 200+1.3 0 | 11.0+1.2 0 | 4.0 | 1.6 | 2.5 | |
| 225+1.4 0 | 11.5+2.4 0 | 4.5 | 1.6 | 2.5 | |
| 250+1.4 0 | 12.0+1.3 0 | 5.0 | 1.6 | 3.5 | |
| 280+1.5 0 | 12.5+2.6 0 | 5.6 | 1.6 | 3.5 | |
| 315+1.6 0 | 13.0+1.4 0 | 6.3 | 1.25 | 3.5 | |
| 355+1.6 0 | 14.0+2.8 0 | 7.1 | 1.25 | 3.5 | |
| 400+1.6 0 | 15.0+1.5 0 | 8.0 | 1.25 | 3.5 | |
| 500+1.7 0 | 16.0+1.6 0 | 10.0 | 1.0 | 4.0 | |
| 630+1.8 0 | 17.0+1.7 0 | 12.3 | 1.0 | 4.0 | |
| Nota: Pressio nominalis fistulae compositae maxima pressionis permissa est pro fistula aquaria in 20° . Si temperatura mutatur, pressionis laborat ut secundum coëfficientem diversarum materiarum temperaturarum pressuram corrigatur. S value: distantia a diametro supplementi ad exteriorem fistulam. | |||||
| Physica et mechanica perficiendi requisita | ||
| Project | Euismod | |
| Anulus rigor, KN/m2 | >8 | |
| Test plana | Non rumpitur | |
| DECREMENTUM longitudinale (100°, conservare 1h) | <0.3% | |
| HYDRAULICUS test | Temperature: 20°С; Tempus: 1h; Pressura nominal x2 | Non rumpitur |
| Temperature: 80°С; Tempus: 165h; Pressura: Nominal pressura x2x0.71 (reduction factor) | ||
| Ruptis pressura test | Temperature: 20°С, pressionis ≥ pressionis nominalis x3.0 . erupit | Blasting |
| Oxidationis inductio temporis (200°С), min | ≥20 | |
| * Tempestas resistentia* Cumulativa acceptio tibiarum≥3.5J/m2 Post industria canus | Hydraulica probatio, condiciones experimentales eaedem sunt ac item 3 in hac tabula | Non rumpitur |
| Rupta pressionis test, condiciones test eaedem sunt ac item 4 in hac tabula | Non inspiratione | |
| Oxidationis inductio temporis (200°С), min | ≥10 | |
* Tantum pro hyacintho pipe composito *